What is Workability of Concrete? | Requirements and Factors Affecting Workability of Concrete

Workability of Concrete


What is Workability of Concrete?


The workability of concrete can be defined as the property of fresh concrete mix that will meet the diverse requirements of mixability, stability, transportability, placeability, mobility, compactability and Finishability of the fresh concrete. This property of the concrete is composite in nature. All the aspects that are included in workability of concrete cannot be explained in a single definition.

As per Indian Standard Code, IS: 6461 (Part V11) -1973,

Workability can be defined as that property of freshly mixed concrete or mortar which determines the ease and the homogeneity with which it can be properly mixed, placed, compacted and finished.


The optimum amount of workability will change from one situation to other. The workability required for a mix that is required to pumped into large sections with reinforcement in minimum amount will not be equal to the workability of a mix that is needed to be poured into a thin section that is reinforced heavily. 

The terms Consistency and Plasticity might be used to express the workability of a concrete mix. But the consistency refers to how wet the mix is and a mix that is merely consistent may not have all the requirement mentioned in the initial statement. A very wet mix will result in segregation and bleeding when they are placed in the formwork. The plasticity is the property of cohesiveness in order to hold the individual grains of the mix together in the whole cement matrix.


Factors Affecting The Workability


There are certain factors that will affect the workability of concrete. The concrete workability is primarily dependent on the materials use in concrete mix, their mix proportions and the environmental conditions. Each factors and their influence on concrete workability are mentioned briefly.

Influence of Mix Proportions on the Workability of Concrete



In the case of a concrete mix, that consist of cement - aggregate - water system, the aggregates will occupy mostly 70 to 75 % of the total volume of the concrete. And it is always recommended to have larger quantities of aggregates to achieve economy.

The total specific area of the aggregates used has to be reduced. This is done by the Proper choice of the shape, size and the proportion of both the fine and the coarse aggregates. The void content in the mix can be reduced by using different size fractions. A highly densely packed particles will require more water content to overcome the difficulty in mobility. The figure - 2 below shows the effect of aggregate cement ratio on the workability.



The intrinsic properties of the cement paste and the workability requirement is determined by the water - cement ratio of the mix.That is is there enough cement paste in order to surround the aggregates in the mix and also for filling up the voids.

The water content is the primary factor that will govern the workability of the fresh concrete. The workability will increase with the increase in the water content.

Influence of Properties of Aggregate on the Workability of Concrete


The effect of aggregates on the properties of aggregates can be briefly enlisted as below:

  1. The use of coarser aggregates of large size or rounded aggregates for the same volume of the aggregates will help in increasing the workability. These aggregate type reduces the specific area and the particle interference. The workability is decreased by the use of elongated aggregates as they have larger particle interference.
  2. The specific surface are will increase by the use of finer particles. This will demand of higher water content.
  3. As specific area  have an important role over workability, the grading of aggregates tend to have critical importance compared to the grading of the coarse aggregates. Or the ratio of C.A : F.A must be chosen so that there is no increase in the specific area.
  4. In general condition those mixes with higher water cement ratio supposed to have fine gradinf and those with lower water-cement ratio have coarser grading. The effect of water content and the aggregate size on the workability is shown in the figure-3 below.

Fig.3: Effect of Water Content and Size of Aggregates on the Workability of Concrete



Influence of Environmental Conditions on the Workability of Concrete


The water content of the concrete mix have to be increased on a hot day so that the desired workability is maintained. The amount of mixing water that is used to bring a change in the mix also will affect the temperature.


Influence of Time on the Workability of Concrete


With time there is loss of water content from the mix. This is because of the evaporation process going on with time. A part of the water is absorbed by the aggregates, some is lost for evaporation and some is taken for the hydration process. The loss of water will depend on the Type of Cement,Amount of Cement, Concrete Mix Proportion, Workability and Temperature.On a average, a 120mm slump concrete mix might lose 50mm slump in the first one of the casting. In terms of compacting factor, the workability will decrease by 0.10 during 1 hour. This is more pronounced for the concrete with plasticisers.
                                                      

Requirements of Workability


The Requirements of Workability are:


  • The workability of the concrete must be such a way that it can be properly mixed, placed in the formwork and properly compacted with less effort without the chances for segregation and bleeding.     
  • The workability is chosen based on the compacting equipment, section size and reinforcement concentration
  • Workability is high for sections that are heavily reinforced or when they have inaccessible parts
  • The workability requirement should be dealt with situation. Minimum workability with satisfactory placement and compaction must be followed.
 Read Article :Segregation in Fresh Concrete and Bleeding in Fresh Concrete


The Table -1 shows the requirements of workability for different conditions of concrete placement.

Table.1: Requirements of workability for different conditions of concrete placement.

Degree of Workability
Slump, mm
Compaction Factor
Suitability

Very Low
0-25
0.78
Roads that are vibrated by power operated machines
Low
25-50
0.85
Roads that are vibrated with hand operated machines, light reinforced sections with vibrations, mass foundation without vibration
Medium
50-100
0.92
Flat slabs, less workable, manually compacted areas
High
100-180
0.95
Sections of Congested Reinforcement. Not for Vibration















About Us

This is a center to bring up and collect all bits of knowledge and technologies flourished and flourishing to reach out for those who wish to acquire knowledge in a broader way. I am a structural engineer by profession and would like to share all information I have acquired all these years till date. This site also aims in researching new topics, works on your questionnaires and fill it up with good facts and information.